Title: Fatigue of additively manufactured 316L stainless steel : the influence of porosity and surface roughness
Authors: Solberg, K
Guan, S 
Razavi, SMJ
Welo, T
Chan, KC 
Berto, F
Issue Date: 2019
Source: Fatigue & fracture of engineering materials & structures, Sept. 2019, v. 42, no. 9, p. 2043-2052
Abstract: The fatigue behaviour of additively manufactured (AM) 316L stainless steel is investigated with the main emphasis on internal porosity and surface roughness. A transition between two cases of failure are found: failure from defects in the surface region and failure from the internal defects. At low applied load level (and consequently a high number of cycles to failure), fatigue is initiating from defects in the surface region, while for high load levels, fatigue is initiating from internal defects. Porosities captured by X-ray computed tomography (XCT) are compared with the defects initiating fatigue cracks, obtained from fractography. The fatigue data are synthesised using stress intensity factor (SIF) of the internal and surface defects on the fracture surface.
Keywords: 316L stainless steel
Fatigue
Porosity
Selective laser melting
Surface roughness
Publisher: Wiley-Blackwell
Journal: Fatigue & fracture of engineering materials & structures 
ISSN: 8756-758X
EISSN: 1460-2695
DOI: 10.1111/ffe.13077
Rights: This is an open access article under the terms of the Creative Commons Attribution License (https://creativecommons.org/licenses/by/4.0/), which permits use, distribution and reproduction in any medium, provided the original work is properly cited.
©2019 The Authors Fatigue & Fracture of Engineering Materials & Structures Published by John Wiley & Sons Ltd.
The following publication Solberg, K., Guan, S., Razavi, S. M. J., Welo, T., Chan, K. C., & Berto, F. (2019). Fatigue of additively manufactured 316L stainless steel: the influence of porosity and surface roughness. Fatigue & Fracture of Engineering Materials & Structures, 42(9), 2043-2052 is available at https://dx.doi.org/10.1111/ffe.13077
Appears in Collections:Journal/Magazine Article

Files in This Item:
File Description SizeFormat 
Solberg_Fatigue_Additively_Manufactured.pdf4.19 MBAdobe PDFView/Open
Open Access Information
Status open access
File Version Version of Record
Access
View full-text via PolyU eLinks SFX Query
Show full item record

Page views

105
Citations as of May 22, 2022

Downloads

102
Citations as of May 22, 2022

SCOPUSTM   
Citations

50
Citations as of May 20, 2022

WEB OF SCIENCETM
Citations

48
Citations as of May 19, 2022

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.