Title: | Effects of postdeposition annealing on the dielectric properties of antiferroelectric lanthanum-doped lead zirconate stannate titanate thin films derived from pulsed laser deposition | Authors: | Yao, Y Lu, SG Chen, H Wong, KH |
Issue Date: | 15-Nov-2004 | Source: | Journal of applied physics, 15 Nov. 2004, v. 96, no. 10, p. 5830-5835 | Abstract: | Lanthanum-doped lead zirconate stannate titanate antiferroelectric thin films were deposited onto Pt-buffered silicon substrates using the pulsed laser deposition method. The deposition temperature was 570 °C. The postdeposition annealing process was carried out in an oxygen-flow tube furnace at temperatures ranging from 650 to 800 °C for a duration of 30 min; its effects were studied through the variations of the microstructure as well as the electrical and dielectric properties. It was found that an appropriate annealing process at temperatures above 700 °C could substantially improve the dielectric properties. However, annealing beyond 800 °C caused the film properties to deteriorate severely. Explanations were given with regard to the microstructure-property relationship. | Keywords: | Lead compounds Lanthanum compounds Antiferromagnetic materials Ferroelectric thin films Pulsed laser deposition Dielectric hysteresis Dielectric polarisation Leakage currents Dielectric losses Permittivity Surface morphology Annealing Crystallisation |
Publisher: | American Institute of Physics | Journal: | Journal of applied physics | ISSN: | 0021-8979 | EISSN: | 1089-7550 | DOI: | 10.1063/1.1804226 | Rights: | © 2004 American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics. The following article appeared in Y. Yao et al., J. Appl. Phys. 96, 5830 (2004) and may be found at http://link.aip.org/link/?jap/96/5830. |
Appears in Collections: | Journal/Magazine Article |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Yao_Effects_postdeposition_annealing.pdf | 315.5 kB | Adobe PDF | View/Open |
Page views
67
Last Week
2
2
Last month
Citations as of May 28, 2023
Downloads
147
Citations as of May 28, 2023
SCOPUSTM
Citations
2
Last Week
0
0
Last month
0
0
Citations as of Jun 1, 2023
WEB OF SCIENCETM
Citations
2
Last Week
0
0
Last month
0
0
Citations as of Jun 1, 2023

Google ScholarTM
Check
Altmetric
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.