Title: | Enhanced mechanical and corrosion properties via annealing treatment on the hot-rolled Ti-Zr-Mo alloy | Authors: | Yue, Y Qi, M Song, T Chen, B Tang, Y Xia, C |
Issue Date: | Apr-2023 | Source: | Materials, Apr. 2023, v. 16, no. 7, 2597 | Abstract: | In this work, the Ti-20Zr-15Mo alloy in its hot-rolled state was annealed in different phase zones, and the effects of the annealing treatment on the phase composition, organization, mechanical and corrosion resistance properties of the alloy were systematically investigated. The results showed that the original β grains of the alloy had all recrystallized to form the β equiaxial grains when annealed at 800 °C, and the grains had been significantly refined. This allowed the alloy to reach a tensile strength of 1000 MPa, a maximum of 28% after stretching, and a significant increase in plasticity. Also, due to the single beta phase, there was no galvanic corrosion, making the alloy annealed at 800 °C have the best corrosion resistance. | Keywords: | Corrosion resistance Microstructure Tensile performance Ti-Zr alloys |
Publisher: | Molecular Diversity Preservation International (MDPI) | Journal: | Materials | EISSN: | 1996-1944 | DOI: | 10.3390/ma16072597 | Rights: | © 2023 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/). The following publication Yue Y, Qi M, Song T, Chen B, Tang Y, Xia C. Enhanced Mechanical and Corrosion Properties via Annealing Treatment on the Hot-Rolled Ti-Zr-Mo Alloy. Materials. 2023; 16(7):2597 is available at https://doi.org/10.3390/ma16072597. |
Appears in Collections: | Journal/Magazine Article |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
materials-16-02597.pdf | 16.47 MB | Adobe PDF | View/Open |
Page views
9
Citations as of Jul 7, 2024
Downloads
2
Citations as of Jul 7, 2024
SCOPUSTM
Citations
1
Citations as of Jul 4, 2024
WEB OF SCIENCETM
Citations
1
Citations as of Jul 4, 2024
![](/image/google_scholar.jpg)
Google ScholarTM
Check
Altmetric
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.