Evaluating and modeling the degradation of PLA/PHB fabrics in marine water

Abstract

Developing degradable bio-plastics has been considered feasible to lessen marine plastic pollution. However, unanimity is still elusive regarding the actual degradability of bio-plastics such as polylactide (PLA) and poly(hydroxybutyrate) (PHB). Thus, herein, we studied the degradability of fabrics made from PLA/PHB blends in marine seawater. The dry-mass percentage of the PLA/PHB fabrics decreased progressively from 100% to 85~90% after eight weeks of immersion. Two environmental aging parameters (UV irradiation and aerating) were also confirmed to accelerate the abiotic hydrolysis of the incubated fabrics. The variation in the molecular structure of the PLA/PHB polymers after the degradation process was investigated by electrospray ionization mass spectrometry (ESI-MS). However, the hydrolysis degradability of bulky PLA/PHB blends, which were used to produce such PLA/PHB fabrics, was negligible under identical conditions. There was no mass loss in these solid PLA/PHB plastics except for a decrease in their tensile strength. Finally, a deep learning artificial neural network model was proposed to model and predict the nonlinear abiotic hydrolysis behavior of PLA/PHB fabrics. The degradability of PLA/PHB fabrics in marine water under the synergistic destructive effects of seawater, UV, and dissolved oxygen provides a pathway for more sustainable textile fibers and apparel products.