Title: | Dielectric behavior and microstructure of (Bi[sub ½]Na[sub ½])TiO₃-(Bi[sub ½]K[sub ½])TiO₃-BaTiO₃ lead-free piezoelectric ceramics | Authors: | Wang, XX Choy, SH Tang, X Chan, HLW |
Issue Date: | 28-Apr-2005 | Source: | Journal of applied physics, 28 Apr. 2005, v. 97, 104101, p. 1-4 | Abstract: | (0.95−x)(Bi[sub ½]Na[sub ½])TiO₃-x(Bi[sub ½]K[sub ½])TiO₃-0.05BaTiO₃ lead-free piezoelectric ceramics (abbreviated as BNT-BKT-BT100x with x varying from 0 to 20 mol %) are prepared by a solid-state reaction process. Variation of the dielectric properties and microstructure of BNT-BKT-BT100x ceramics with BKT content is studied. The results indicate that the relative permittivity ε[sub r] and loss tangent tan δ vary with the BKT amount. Scanning electron microscope observation also indicates that BKT in high amount affects the microstructure. X-ray diffraction analysis shows that the incorporated BKT diffuses into the BNT-BT lattice to form a solid solution during sintering. | Keywords: | Bismuth compounds Sodium compounds Potassium compounds Barium compounds Piezoceramics Crystal microstructure Permittivity Sintering Dielectric losses X-ray diffraction Scanning electron microscopy |
Publisher: | American Institute of Physics | Journal: | Journal of applied physics | ISSN: | 0021-8979 | EISSN: | 1089-7550 | Rights: | © 2005 American Institute of Physics. This article may be downloaded for personal use only. Any other use requires prior permission of the author and the American Institute of Physics. The following article appeared in X.X. Wang et al. J. Appl. Phys. 97, 104101 (2005) and may be found at http://link.aip.org/link/?jap/97/104101 |
Appears in Collections: | Journal/Magazine Article |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
dielectric-behavior_05.pdf | 263.83 kB | Adobe PDF | View/Open |
Page views
115
Last Week
1
1
Last month
Citations as of May 5, 2024
Downloads
66
Citations as of May 5, 2024
SCOPUSTM
Citations
95
Last Week
0
0
Last month
1
1
Citations as of Apr 26, 2024
WEB OF SCIENCETM
Citations
85
Last Week
2
2
Last month
0
0
Citations as of May 2, 2024
Google ScholarTM
Check
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.