Title: Resistive switching behaviour in oxide thin films and devices
Authors: Lau, Hon-kit
Degree: M.Phil.
Issue Date: 2010
Abstract: Resistive switching effect induced by voltage pulses has been praised as one of the potential candidates for the next-generation non-volatile memories. Resistive random access memory (RRAM) based on transition-metal perovskite oxides has demonstrated a large resistance change upon the application of small and short voltage pulses with different polarities. Some of the advantages of the effect include its fast response, low power consumption, high information packing density and non-volatile characteristics. However, the resistive switching mechanism is still under debate, and the devices have to be optimized before they can be used commercially. The objective of this work is to study the properties of resistive switching effect based on perovskite manganites including Pr0.7Ca0.3MnO3 (PCMO) and La0.7Sr0.3MnO3 (LSMO), and to investigate the resistive switching mechanism. The research work includes the fabrication and subsequent characterization of PCMO and LSMO oxide thin film-based devices. The performance of the switching devices, including pulse magnitude and pulse width dependences of resistance ratio, data retention ability, and their durability towards repeated switching, have been studied. Moreover, the dependence of the switching effect on metal electrodes has been studied. For resistive switching mechanism analysis, thermal measurements including micro-thermocouples and thermoreflectance imaging techniques were used. By studying the temperature variation in the devices under different voltage biases, AlOx was found to exist at the Al/PCMO interface, and it is proposed that electrochemical reaction of AlOx is contributing to the resistive switching effect in Al-based resistive switching devices.
Subjects: Hong Kong Polytechnic University -- Dissertations
Thin film transistors
Thin films -- Thermal properties
Pages: xi, 123 leaves : ill. (some col.) ; 30 cm.
Appears in Collections:Thesis

Show full item record

Page views

4
Citations as of May 15, 2022

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.