Title: Development of high dispersed TiO2 paste for transparent screen-printable self-cleaning coatings on glass
Authors: Wang, Y
Lu, L 
Yang, H 
Che, Q
Keywords: Ball mill process
Powder technology
Screen-printing
Self-cleaning coating
Issue Date: 2013
Publisher: Springer
Source: Journal of nanoparticle research, 2013, v. 15, no. 1, 1384 How to cite?
Journal: Journal of Nanoparticle Research 
Abstract: This paper reports a cheap and facile method to fabricate transparent self-cleaning coatings on glass by screen-printing high dispersed TiO 2 paste. Three kinds of ZrO2 beads with diameter of 2, 1, and 0.1-0.2 mm were utilized to investigate their influence on the grinding and dispersion of the commercial TiO2 powder in the ball mill. From the SEM images, surface profiler and transmittance spectrum it could be demonstrated that the smallest ZrO2 bead with the diameter of 0.1-0.2 mm was the best candidate to disperse the TiO2 powder into nanoscale size to make the high dispersed TiO2 paste which was the key factor to achieve a smooth, high transparent TiO2 coating. The surface wettability measurement showed that all the screen-printed coatings had super hydrophilic surfaces, which was independent to the surface morphology. However, the coating with the highest transparency showed the lowest photocatalytic activity which is mainly due to the light loss.
URI: http://hdl.handle.net/10397/8546
ISSN: 1388-0764
DOI: 10.1007/s11051-012-1384-5
Appears in Collections:Journal/Magazine Article

Access
View full-text via PolyU eLinks SFX Query
Show full item record

SCOPUSTM   
Citations

9
Last Week
0
Last month
0
Citations as of Dec 8, 2018

WEB OF SCIENCETM
Citations

7
Last Week
0
Last month
1
Citations as of Dec 15, 2018

Page view(s)

139
Last Week
1
Last month
Citations as of Dec 10, 2018

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.