Title: Preparation and properties of (Sr_0.2Ba_0.8) TiO_3 solution
Other Titles: 鈦酸鍶鋇溶膠制備研究
Authors: Li, K
Chan, HLW 
Choy, CL 
Li, JH
Keywords: Sol-Gel film
(Sr0.2Ba0.8)TiO3
Issue Date: 2000
Publisher: 江苏工业学院
Source: 江苏工业学院学报, 2000, v. 12, no. 1, p. 1-4 How to cite?
Journal: 江苏工业学院学报 
Abstract: Using organic salts of strontium and barium with titanium butoxide as precursors, the solution of Sr -modified BaTiO3 were prepared successfully. The effect of organic acid and the preparing procedures on the properties (such as stickiness, moist - sensitivity, CO2 - sensitivity) of solutions was detected. The results show that the qualified solutions could be prepared by hydrolyzing titanium butoxide in ethyl acetate partially and then mixing the former with the Ba and Sr organic salts (CxH2xCOO-, x = 7 - 8) in the same solvent sufficiently. Using the solutions, Pt/BST/Al capacitor and Si/BST/Al capacitor were prepared. The dielectric constant of BST is about 280 on Pt and 96 on Si. The leakage current of capacitors is lower than 10-8A/cm2 for 0.56 μm BST film.
URI: http://hdl.handle.net/10397/63739
ISSN: 1005-8893
EISSN: 1673-9620
Appears in Collections:Journal/Magazine Article

Access
View full-text via PolyU eLinks SFX Query
Show full item record

Page view(s)

27
Last Week
1
Last month
Checked on Oct 16, 2017

Google ScholarTM

Check



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.