Please use this identifier to cite or link to this item: http://hdl.handle.net/10397/3710
Title: Studies of TGS/P(VDF-TrFE) and MMT/P(VDF-TrFE) 0-3 composites
Authors: Yang, Yan
Keywords: Hong Kong Polytechnic University -- Dissertations
Ferroelectric crystals
Triglycine sulfate
Montmorillonite
Issue Date: 2005
Publisher: The Hong Kong Polytechnic University
Abstract: Ferroelectric ceramic/polymer composites have been widely studied in recent years due to the combination of good mechanical performance and high electroactive capabilities. In this project, triglycine sulfate (TGS)/poly(vinylidene fluoride-trifluoroethylene) (P(VDF-TrFE), 70/30 mol%) 0-3 composites with various volume percents of TGS were fabricated by compression moulding. Three series of composites were prepared: (I) unpoled composites, (II) composites with only the TGS phase poled and (III) composites with both phases poled. The structure, phase transitions and dielectric, piezoelectric and pyroelectric properties of the composites were investigated. Scanning electron microscope (SEM) studies of the composites showed that the TGS particles were uniformly dispersed in the copolymer matrix. The reflection peaks of both the TGS and P(VDF-TrFE) phase appeared in the X-ray diffraction (XRD) patterns of the composites and the phase transitions of the two phases were observed in the differential scanning calorimetry (DSC) thermograms of the composites. The relative permittivity and pyroelectric coefficient of the composites were found to increase with increasing TGS content. The relative permittivity and pyroelectric coefficient were compared with the theoretical predictions of the Bruggeman model and the effective medium model, respectively, and good agreement was obtained. It was also found that if the two phases were poled in the same direction, the pyroelectric contributions from TGS and P(VDF-TrFE) reinforced while piezoelectric contributions partially canceled. Thus the composite with 43 vol% of TGS exhibited a high pyroelectric coefficient and high pyroelectric figures of merit together with a low piezoelectric coefficient. The low piezoelectric activity is a significant advantage in pyroelectric sensor application since it will give rise to a low vibration induced noise. Montmorillonite (MMT)/P(VDF-TrFE) (80/20 mol%) 0-3 nanocomposites with 1 wt% and 4 wt% of MMT were also fabricated. Na⁺-MMT was first modified with cetyltrimethylammonium bromide (CTAB) before being incorporated into the copolymer matrix. The nanocomposites were characterized by means of XRD and DSC. The dielectric permittivity, polarization hysteresis, piezoelectric coefficient and pyroelectric coefficient were also measured. The XRD patterns showed that P(VDF-TrFE) copolymer chains had been intercalated into the layered nanostructures of the CTAB treated MMT. The DSC thermograms indicated that the Curie temperature of the nanocomposites were higher than that of the pure copolymer. The relative permittivity and remnant polarization of the nanocomposites were found to increase with MMT content. The piezoelectric coefficient and pyroelectric coefficient were also enhanced in the MMT/P(VDF-TrFE) nanocomposites.
Description: xvii, 125 leaves : ill. ; 30 cm.
PolyU Library Call No.: [THS] LG51 .H577M AP 2005 Yang
URI: http://hdl.handle.net/10397/3710
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b17938089_link.htmFor PolyU Users 162 BHTMLView/Open
b17938089_ir.pdfFor All Users (Non-printable) 3.91 MBAdobe PDFView/Open
Show full item record

Page view(s)

411
Last Week
3
Last month
Checked on Sep 24, 2017

Download(s)

170
Checked on Sep 24, 2017

Google ScholarTM

Check



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.