Title: Study of PZT multilayer piezoelectric transformers
Authors: Zhang, Yu
Keywords: Electric transformers
Piezoelectric materials
Hong Kong Polytechnic University -- Dissertations
Issue Date: 2001
Publisher: The Hong Kong Polytechnic University
Abstract: Two types of lead zirconate titanate (PZT) multilayer structures have been investigated in this work. The first one, which consisted of thick PZT films fabricated by roll-casting and platinum (Pt) interleaving electrodes, was sintered at high temperature (1280°C). Thickness mode and length mode multilayer transformers have been fabricated from this type of multilayer structure and tested. The second type of multilayer PZT structure was fabricated by a sol-gel technique. A conductive oxide, lanthanum nickel oxide (LNO), was used as the electrode and the PZT/LNO multilayers were co-fired at below 650°C to make the process compatible with the integrated circuit (IC) technology. Original contributions reported in this thesis included: (1) Besides fabricating and evaluating PZT multilayer transformers based on the usual thickness mode, a new length mode multilayer transformer has been fabricated and its performance characterized. (2) A PZT/LNO multilayer structure was studied. A buffer layer consisting of a mixture of PZT and LNO was introduced at the interface to enhance the adhesion between the PZT and LNO. (3) To fabricate LNO films thick enough to be used as electrode, a modified sol-gel process has been used. LNO powder was introduced into the LNO sol-gel solution to induce a seeding effect in the film formation process and the annealing temperature has been reduced.
Description: xv, 122 leaves : ill. ; 30 cm.
PolyU Library Call No.: [THS] LG51 .H577M AP 2001 Zhang
URI: http://hdl.handle.net/10397/3703
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b15650327_link.htmFor PolyU Users 162 BHTMLView/Open
b15650327_ir.pdfFor All Users (Non-printable) 3.56 MBAdobe PDFView/Open
Show full item record

Page view(s)

441
Last Week
2
Last month
Checked on Feb 19, 2017

Download(s)

220
Checked on Feb 19, 2017

Google ScholarTM

Check



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.