Title: Optical properties of lead magnesium niobate-lead titanate (PMN-PT) and strontium barium niobate (SBN) thin films
Authors: Chan, Ka-yi
Keywords: Hong Kong Polytechnic University -- Dissertations
Thin films -- Optical properties
Pulsed laser deposition
Issue Date: 2005
Publisher: The Hong Kong Polytechnic University
Abstract: Epitaxial (1-x)Pb(Mg₁/₃Nb₂/₃)O₃-xPbTiO₃((1-x)PMN-xPT) films x=0.1,0.3,0.35 and 0.4 grown under different deposition temperatures (630 °C to 710 °C) were fabricated on MgO substrates using pulsed laser deposition (PLD). X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM) were employed to characterize the structural properties of these (1-x)PMN-xPT films. Our results show that these films possess excellent structural properties and are cube-on-cube grown on MgO substrates. Spectroscopic ellipsometer (SE) was used to characterize the depth profiles, the microstructural inhomogeneities, including void and surface roughness, refractive indicies and extinction coefficients of the films. In the analysis of the measured SE spectra, a double-layer Lorentz model was adopted to represent the optical properties of the (1-x)PMN-xPT films. On the basis of these results, the effects of PT composition and deposition temperature on the optical properties of (1-x)PMN-xPT were revealed. Our measurements show that the refractive indices of the (1-x)PMN-xPT films increase with PT contents. This dependence is consistent with our optical transmission measurements which revealed decreasing energy band gaps of the (1-x)PMN-xPT films with increasing PT content. Our ellipsometric measurements show that a maximum refractive index of the (1-x)PMN-xPT films is obtained at a deposition temperature of 670 °C. No observable change in the band gap energy for various deposition temperatures is detected. This last feature is also confirmed by our independent optical transmission measurements. Thus the change in refractive index due to deposition temperature is attributed to the change in structural properties. Sr₀.₆Ba₀.₄Nb₂O₆ (SBN60) films of different annealing temperature (200 °C to 700 °C) and durations (0.5 h to 10 h) were fabricated by the sol-gel technique. Our structural characterizations show that these films are amorphous for annealing temperatures ≤ 500 °C, and polycrystalline for annealing temperatures ≥ 600 °C. In the analysis of the measured SE spectra, a triple-layer Lorerntz model was used to interpret the optical properties of the SBN6O films. SE measurements reveal that the refractive indices of SBN6O films increase with annealing temperature. The increase is more significant at around the crystallization temperature of the films, i.e. between 500 °C and 600 °C. The extinction coefficients also possess a similar trend showing zero values for amorphous films and large values (for example, 0.1 at 2.5 eV) for films annealed above 600 °C. Our results demonstrate that the crystallization of the films has an important influence on the refractive index as well as extinction coefficient. Although crystallization can raise the refractive index of the film because of the film densification, it also promotes scattering due to a larger extinction coefficient. Similar phenomena are confirmed by annealing the films for different durations.
Description: vii, 126 leaves : ill. (some col.) ; 30 cm.
PolyU Library Call No.: [THS] LG51 .H577M AP 2005 Chan
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b17937802_link.htmFor PolyU Users 162 BHTMLView/Open
b17937802_ir.pdfFor All Users (Non-printable) 4.86 MBAdobe PDFView/Open
Show full item record
PIRA download icon_1.1View/Download Contents

Page view(s)

Last Week
Last month
Citations as of Sep 17, 2018


Citations as of Sep 17, 2018

Google ScholarTM


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.