Title: Studies of PMN-PT/polymer composites
Authors: Lam, Kwok-ho
Keywords: Hong Kong Polytechnic University -- Dissertations
Piezoelectric ceramics
Pyroelectricity
Ferroelectric crystals
Issue Date: 2002
Publisher: The Hong Kong Polytechnic University
Abstract: Lead magnesium niobate-lead titanate (PMN-PT) wit nominal composition of 0.65PMN-0.35PT (abbreviated as PMN-PT) is studied in this project. This composition of PMIN-PT with around 35mo1 % PT is at its morphotrophic phase boundary (MPB) region where it has very high dielectric and piezoelectric properties. In this work, four kinds of samples were fabricated. These include PMN-PT ceramic discs and fibres, PMN-PT / vinylidene fluoride-trifluoroethylene P(VDF-TrFE) 0-3 composites and PMN-PT/ epoxy 1-3 composites. PMIN-PT ceramic powders were prepared by the Columbite method and by the modified sol-gel method. PMIN-PT discs were fabricated using the dry pressing and sintering method. The dielectric and piezoelectric properties of the ceramics were evaluated and the data were used as references in the composite modeling. PMN-PT/epoxy 1-3 composites with ceramic volume fractions ranged from 0.43 to 0.86 were fabricated by a dice-and-fill method. The resonance characteristics of the 1-3 composites were studied by progressively thinning down the composite samples. The modified parallel and series model calculation was used to compare with the measured parameters of the dice-and-fill 1-3 composites. PMN-PT ceramic fibres were fabricated by a modified sol-gel method in which metal alkoxides were used as the starting precursor solutions. Fine oxide powders were mixed with the solution and the gel fibres containing oxide powders were extruded. With this method, crack-free PMN-PT fibres (~100um diameter) could be fabricated after proper heat treatments. Crack-free PMN-PT fibres were incorporated into an epoxy matrix to form 1-3 composites. Ceramic volume fractions ranged from 0.12 to 0.42 were achieved. Using the measured parameters of the epoxy and the 1-3 composites, the relative permittivity, elastic and piezoelectric properties of a single PMN-PT fibre were found. The PMN-PT / P(VDF-TrFE) 0-3 composites were prepared using solvent casting. PMIN-PT powders prepared by the Columbite method were dispersed uniformly in the copolymer matrix and bulk composites are fabricated by hot pressing. Composites with PMN-PT volume fraction of 0.05 to 0.4 have been fabricated. Since the piezoelectric coefficients of ceramics and copolymer are opposite in sign, properties of the 0-3 composites can be modified using different poling conditions. The electric fields acting on the ceramic inclusions and the copolymer matrix were estimated by model calculation. The variation of the coercive field of the 0-3 composites against the PMN-PT volume fraction was also calculated. Original results on the study of PMN-PT ceramics and several kinds of composites have been reported in the thesis.
Description: xxx, 248 leaves : ill. ; 30 cm.
PolyU Library Call No.: [THS] LG51 .H577M AP 2002 Lam
URI: http://hdl.handle.net/10397/3355
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b16576755_link.htmFor PolyU Users 162 BHTMLView/Open
b16576755_ir.pdfFor All Users (Non-printable) 8.1 MBAdobe PDFView/Open
Show full item record

Page view(s)

495
Last Week
3
Last month
Checked on Nov 19, 2017

Download(s)

189
Checked on Nov 19, 2017

Google ScholarTM

Check



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.