Title: Laser fabrication of surface metal matrix composites on aluminum alloy
Authors: Chong, Pak-hung
Keywords: Aluminum alloys
Metallic composites
Hong Kong Polytechnic University -- Dissertations
Issue Date: 2001
Publisher: The Hong Kong Polytechnic University
Abstract: The creation of a wear resistant surface of metal matrix composite on AA6061 aluminum alloy by laser surface cladding of pre-pasted metal/ceramic powder was successfully achieved using a 2 kW CW Nd-YAG laser. Different ratios of metal and ceramic powder were investigated. Powder mixtures of different compositions of Mo/WC, Mo/TiC, Mo/Si₃N₄ and Si₃N₄/TiC were pre-placed on the aluminum alloy AA6061 and then irradiated by the defocused laser beam. For the Mo/WC laser cladding system, the processing parameters were 17 mm/s beam scanning speed, 3 mm beam diameter and 1.4 kW laser power at the workpiece and 0.3 mm pre-placed layer thickness. For the Mo/TiC laser cladding system, the optimum processing parameters were 3 mm laser beam size, 17 mm/s beam scanning speed, 1.3 kW laser power at the workpiece and 0.25 mm pre-placed layer thickness. Both of 2 systems used 50% overlapping on every single track to produce a surface. Mo/Si₃N₄ and Si₃N₄/TiC systems have a preliminary studied and proved that they are difficult to produce a good clad layer. The chemical composition, microstructure and surface morphology of the clad layer were analyzed using scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray diffractometry (XRD). High quality metal matrix composite (MMC) coatings of Mo/WC and Mo/TiC on the Al alloy were obtained. The clad layers were free of porosity and crack. Excellent bonding between the coating and the aluminum alloy substrate was ensured by the strong metallurgical interface. The values of surface hardness of the clad specimens were increased significantly. The samples have been characterized by abrasive pin-on-disc wear test. The results show that all clad specimens have extremely good abrasive wear resistance. Mostly, fine dendritic structures were observed in the MMC clad layer. Depending on the process parameters, unmelted or partially melted WC particles were also observed. These unmelted particles were found to contribute to the improvement of the wear resistance. The distributions of the dendrites and unmelted or partially melted ceramic phases were found to depend on the process parameters. For the Mo/WC and Mo/TiC MMC cladding systems, the matrix of the MMC layer consisted of alloys of Mo-W-Al and Mo-Ti-Al respectively, which are harder than the Al alloy. Clad layers using Mo/Si₃N₄ and TiC/Si₃N₄ systems were mostly porous and had cracks. Interfacial bonding between the clad surface and the substrate was poor. It was unsuccessful to fabricate a surface large enough for wear test.
Description: xiv, 157 leaves : ill. ; 30 cm.
PolyU Library Call No.: [THS] LG51 .H577M MFG 2001 Chong
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b1599532x_link.htmFor PolyU Users 162 BHTMLView/Open
b1599532x_ir.pdfFor All Users (Non-printable) 6.3 MBAdobe PDFView/Open
Show full item record
PIRA download icon_1.1View/Download Contents

Page view(s)

Last Week
Last month
Citations as of Feb 18, 2019


Citations as of Feb 18, 2019

Google ScholarTM


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.