Title: Pulsed laser deposition (PLD) of magnetic multilayer and granular thin films
Authors: Li, Ming-fai
Keywords: Thin films.
Pulsed laser deposition.
Hong Kong Polytechnic University -- Dissertations
Issue Date: 1999
Publisher: The Hong Kong Polytechnic University
Abstract: CoAg granular and multilayer films as well as the Ti/Si based films have been fabricated by pulsed laser deposition (PLD) method. A special split target and a rotating multi-target holder have been developed to facilitate the PLD process. X-ray diffraction and Atomic Force Microscopy (AFM) were used to examine the structure and topography of the films respectively. The electrical properties and the magnetoresistance (MR) of these films were measured by a standard four-probe method. The effects of film thickness, substrate temperature and post-annealing on Ti/Si based films were investigated. In the CoAg granular films a MR ratio of 9% at 77 K and 5.5% at room temperature were obtained under the influence of a magnetic field of 1 Tesla. The PLD CoAg multilayer films in this work however showed a relatively poor MR. Some possible explanations for this result are suggested. Anomalous electrical properties were obtained in the Ti/Si based films. In addition, an unusual and rather large positive magnetoresistance (PMR) was also observed in these samples. Maximum PMR of +37% at about 170 K and +10% at room temperature were recorded. Thin films based on the Ti/Si and other related materials systems can have very good potentials for integrated sensor applications. It is one of the purpose of the present work to explore this material system and to report some of the interesting findings.
Description: ii, 100 leaves : ill. ; 31 cm.
PolyU Library Call No.: [THS] LG51 .H577M AP 1999 Li
URI: http://hdl.handle.net/10397/2983
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b14695741_link.htmFor PolyU Users 161 BHTMLView/Open
b14695741_ir.pdfFor All Users (Non-printable) 3.36 MBAdobe PDFView/Open
Show full item record

Page view(s)

447
Last Week
3
Last month
Checked on Aug 13, 2017

Download(s)

167
Checked on Aug 13, 2017

Google ScholarTM

Check



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.