Title: Corrosion protection of NdFeB permanent magnets
Authors: Cheng, Chung-wai
Keywords: Permanent magnets -- Corrosion.
Magnets -- Corrosion.
Protective coatings.
Hong Kong Polytechnic University -- Dissertations
Issue Date: 1998
Publisher: The Hong Kong Polytechnic University
Abstract: Neodymium-iron-boron (Nd-Fe-B), the most powerful permanent magnet material developed to date, derives its attractiveness from its desirable magnetic properties. However, the poor corrosion resistance of Nd-Fe-B in humid and/or chloride containing environments seriously limits its applications. The present project aims at developing feasible and effective coating systems or methods for improving the corrosion resistance of the Nd-Fe-B magnet so as to widen its scope of applications. Three coating systems or methods have been successfully developed and their efficacy has been evaluated by the salt spray test and electrochemical tests, in comparison with commercial coated samples. (1) The first system developed consists of a duplex Ni(undercoat) / Cr(topcoat) coating electrodeposited by DC plating. It was found that for a Ni(20μm) / Cr(1μm) coating, the magnet did not show signs of corrosion in the salt spray test for more than 360 hours. (2) To further enhance the performance of the Ni layer, pulsed current plating of Ni has been attempted. The corrosion resistance of pulse-Ni plated samples was found to be at least doubled as compared with the DC plated ones of similar thickness. (3) As an alternative to metallic coatings, an organic coating system consisting of a commercial primer and a BMI (bismaleimide) topcoat has been applied on the Nd-Fe-B magnet. For an exposure time of 360 hours in the salt spray test, there was no sign of failure for samples protected with a primer(5μm) / BMI(5μm) coating. All these coatings exhibited excellent adhesion strength as indicated by the scotch tape test and were reasonably scratch-resistant.
Description: 138 leaves : ill. ; 30 cm.
PolyU Library Call No.: [THS] LG51 .H577M AP 1998 Cheng
URI: http://hdl.handle.net/10397/2971
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b14418447_link.htmFor PolyU Users 162 BHTMLView/Open
b14418447_ir.pdfFor All Users (Non-printable) 10.91 MBAdobe PDFView/Open
Show full item record

Page view(s)

700
Last Week
3
Last month
Checked on May 21, 2017

Download(s)

259
Checked on May 21, 2017

Google ScholarTM

Check



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.