Title: Laser surface modification of UNS S31603 stainless steel. Part I : Microstructures and corrosion characteristics
Authors: Kwok, CT
Cheng, FT
Man, HC 
Keywords: Austenitic stainless steel
Laser surface alloying
Microstructures
Pitting corrosion
Issue Date: 2000
Publisher: Elsevier
Source: Materials science and engineering. A, Structural materials : properties, microstructure and processing, 2000, v. 290, no. 1-2, p. 55-73 How to cite?
Journal: Materials science and engineering. A, Structural materials : properties, microstructure and processing 
Abstract: Laser surface alloying using various elements (Co, Ni, Mn, C, Cr, Mo, Si) and alloys/compounds (AlSiFe, Si3N4 and NiCrSiB) on austenitic stainless steel UNS S31603 was attemped. Alloying materials in powder form were preplaced on the surface of the substrate by flame spraying or pasting. The surface was then scanned by a high power laser beam to achieve surface alloying. The microstructures of the alloyed layers were studied by scanning electron microscopy, optical microscopy and X-ray diffractometry, and the corrosion characteristics in 3.5% NaCl solution at 23°C were studied by potentiodynamic polarisation. The performance of the laser alloyed surfaces varied depending on the type and amount of alloying materials used, and on the laser processing parameters. The specimens alloyed with Co, Ni, Mn, C or NiCrSiB contained austenite as the main phase, with carbides and carbides/borides as the minor phases in C-alloyed and NiCrSiB-alloyed specimens. For specimens alloyed with Cr or Mo, the major phase was ferrite. In the case of Si or Si3N4, the major phase was an intermetallic Fe3Si. When A1SiFe was used, the major phase could be ferrite or Fe3Al, depending on the dilution ratio. The larggest improvement in corrosion resistance was achieved with Si and Si3N4, leading to a noble shift in the pitting potential of 170 and 211 mV, respectively, and a corresponding noble shift in the protection potential of 130 and 221 mV. For NiCrSiB, the effect on the corrosion resistance depended on the degree of dilution. For all the other alloying materials, the corrosion resistance either remained unchanged or deteriorated mainly due to the presence of some ceramic or intermetallic phases which acted as sites of pit initiation.
URI: http://hdl.handle.net/10397/27796
ISSN: 0921-5093
EISSN: 1873-4936
DOI: 10.1016/S0921-5093(00)00929-1
Appears in Collections:Journal/Magazine Article

Access
View full-text via PolyU eLinks SFX Query
Show full item record

SCOPUSTM   
Citations

56
Last Week
0
Last month
0
Citations as of Sep 10, 2017

WEB OF SCIENCETM
Citations

22
Last Week
0
Last month
0
Citations as of Jul 28, 2017

Page view(s)

29
Last Week
2
Last month
Checked on Sep 17, 2017

Google ScholarTM

Check

Altmetric



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.