Title: Growth behaviors of ZnO nanostructure on SMAT Cu0.62Zn0.38 during oxidation
Authors: Wang, JP
Xu, CH
Zhu, ZB
Wen, CS
Lu, J
Shi, SQ 
Issue Date: 2013
Publisher: EDP Sciences
Source: European physical journal. Applied physics, 2013, v. 62, no. 2 How to cite?
Journal: European physical journal. Applied physics 
Abstract: Cu0.62Zn0.38 foil was subjected to surface mechanical attrition treatment (SMAT) processing first. Growth behavior of ZnO nanostructure on the SMAT Cu0.62Zn0.38 surface during thermal oxidation was investigated in this paper. The original and SMAT Cu0.62Zn0.38 foils were thermally oxidized at 400 similar to 700 degrees C under various gaseous environments, including nitrogen and mixture of N-2-O-2 at a pressure of 1 atm. for 3 h. The oxidized specimens were characterized with a scanning electron microscope, an X-ray diffractometer and a transmission electron microscope. It is found that nanosheets are easily formed on the SMAT specimen surface. The favorable formation of nanosheets relates to twin lamellae structure of Cu0.62Zn0.38 formed during SMAT processing.
ISSN: 1286-0042
EISSN: 1286-0050
DOI: 10.1051/epjap/2013120539
Appears in Collections:Journal/Magazine Article

View full-text via PolyU eLinks SFX Query
Show full item record

Page view(s)

Last Week
Last month
Citations as of Dec 16, 2018

Google ScholarTM



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.