Title: Mechanical properties of dual ion beam deposited silicon nitride films
Authors: Tsang, Mei-po Mable
Keywords: Thin films
Hong Kong Polytechnic University -- Dissertations
Issue Date: 2001
Publisher: The Hong Kong Polytechnic University
Abstract: Amorphous silicon nitride (SiNx)films with nitrogen-to-silicon ratio (x) varying from 0-1.36 were fabricated by dual ion beam deposition (DIBD) on Si substrates. The composition, structure and many physical properties (i.e. mechanical, etching, optical and electrical properties) of the films were characterized. The hardness and elastic modulus of the hydrogen-free DIBD SiNx films were found to vary from 12.2-21.5 GPa and 191-256 GPa respectively with increasing x. The friction coefficient dropped from 0.58 to 0.38. Owing to peening effect, all the films had compressive stress, which rose from 0.53 to 1.41 GPa with x. These data revealed that DLBD SiNx could be used for surface protective coatings. The etching rate the SiN₁.₃₆ film in buffered hydrofluoric acid (BHF) was above 7 nm min-¹. For KOH at 80°C, the etching rate of all the samples was negligibly small. A model was established to fit the optical absorption spectra and temperature dependence of electrical conductivity of the films with high density of mid-gap states. Results indicated that the optical band gap of DIBD SiNx films rose from 1.8 to 4.2 eV when x increased. Hopping of charge carriers dominated the transport properties of the films. Nanoindentation tests were done on microbridges made of CVD silicon nitride films. The load-unload curves of CVD microbridges were fitted numerically, and the elastic modulus, residual stress and bending strength of the films were derived. This experiment demonstrated the validity of this methodology.
Description: 1 v. (various pagings) : ill. ; 30 cm
PolyU Library Call No.: [THS] LG51 .H577M AP 2001 Tsang
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b15995446_link.htmFor PolyU Users162 BHTMLView/Open
b15995446_ir.pdfFor All Users (Non-printable)3.42 MBAdobe PDFView/Open
Show full item record
PIRA download icon_1.1View/Download Contents

Page view(s)

Last Week
Last month
Citations as of Dec 9, 2018


Citations as of Dec 9, 2018

Google ScholarTM


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.