Title: Luminescence of phosphors based on novel oxides for field emission display
Authors: Li, Hiuling
Keywords: Phosphors.
Luminescence.
Metallic oxides
Field emission
Hong Kong Polytechnic University -- Dissertations
Issue Date: 2009
Publisher: The Hong Kong Polytechnic University
Abstract: This thesis presents studies on the synthesis, structural and optical characterization of rare-earth doped tungstates and binary oxide phosphors. Photoluminescence (PL) and low-voltage cathodoluminescence (CL) are used to investigate these promising phosphors for use in field emission display. The imperfection performance of sulfide-base phosphors has motivated us to investigate the more chemically and physically stable oxide-based phosphors. In our work, a variety of properties of the phosphors were characterized by X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectra, low-voltage CL, PL spectra and lifetime. In our work, the luminescent properties of BaWO₄-based and ZnWO₄-based phosphors were investigated. Rare-earth ions (Eu³⁺ , Tb³⁺ , Tm³⁺) doped BaWO₄phosphors were prepared by a polyol-mediated method. Spherical morphology of the scheelite-structured particles was observed. While excited by ultra-violet (UV) light or low-voltage electron beam, red, green and blue emissions were observed in Eu³⁺, Tb³⁺ and Tm³⁺ doped phosphors, respectively. These emissions are attributed to the characteristic intraconfigurational 4f transitions in Eu³⁺, Tb³⁺ and Tm³⁺. Among them, the luminance of BaWO₄: Tb³⁺ was as high as 4866 cd/m² under excitation of electron beam (4.5 kV). The investigation on the chromaticity of BaWO₄: Tm³⁺ indicated that it had extremely high color purity (97%) and showed its potential as a promising blue-emitting phosphor. For the Eu³⁺ doped BaWO₄, very high intensity ratio of ⁵D₀ → ⁷F₂and ⁵Do → ⁷F₁transitions (R-value) indicates that Eu³⁺ ions may locate at a crystallographic site without inversion symmetry. Wolframite nanostructural ZnWO₄and ZnWO₄: Eu³⁺ were synthesized by refluxing in a water solution and followed by annealing at different temperatures. Different colors of emission were observed from the ZnWO₄- based phosphors. Blue-green CL emission of the annealed ZnWO₄is attributed to the highly emissive WO⁶⁻₆ ion complex. As-synthesized and annealed ZnWO₄: Eu³⁺ phosphors exhibit red and white emissions, respectively. The dynamic of emissions between WO⁶⁻₆ ion complex and Eu³⁺ ions with increasing annealing temperature were discussed. Luminescence of binary oxides was also studied in this work. A urea precipitation method was used to synthesize nanostructural ZrO₂: RE³⁺ (RE=Eu, Tb, Tm) phosphors. The characteristic red-green-blue (RGB) emissions of the rare earth ions were observed in the PL spectrum. Comparing to BaWO₄: Eu³⁺, ZrO₂: Eu³⁺ phosphor has a relatively small R-value, which indicates that Eu³⁺ ions may be distorted slightly and occupy a site without inversion symmetry. Similar result was observed in the CL spectrum. Regarding the Tm³⁺ doped ZrO₂, both emissions from defects of ZrO₂and Tm³⁺ ions was observed; however, such emission was observed in CL. Intrinsic emission in ZnO was also studied via PL and CL. Different morphologies of ZnO particles were synthesized by a hydrothermal method. Defect-related emission of the ZnO particles as a function of crystal size and morphology was discussed.
Description: x, 90, xii leaves : ill. (some col.) ; 31 cm.
PolyU Library Call No.: [THS] LG51 .H577M AP 2009 Li
URI: http://hdl.handle.net/10397/2393
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
b2343000x_link.htmFor PolyU Users162 BHTMLView/Open
b2343000x_ir.pdfFor All Users (Non-printable)14.65 MBAdobe PDFView/Open
Show full item record

Page view(s)

542
Last Week
4
Last month
Checked on May 21, 2017

Download(s)

708
Checked on May 21, 2017

Google ScholarTM

Check



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.