Title: Bifurcation of crack pattern in arrays of two-dimensional cracks
Authors: Muhlhaus, HB
Chau, KT 
Ord, A
Issue Date: 1996
Source: International journal of fracture, 1996, v. 77, no. 1, p. 1-14 How to cite?
Journal: International Journal of Fracture 
Abstract: Theoretical calculations based on simple arrays of two-dimensional cracks demonstrate that bifurcation of crack growth patterns may exist. The approximation used involves the 'dipole asymptotic' or 'pseudo-traction' method to estimate the local stress intensity factor. This leads to a crack interaction parametrized by the crack length/spacing ratio λ = a/h. For parallel and edge crack arrays under far field tension, uniform crack growth patterns (all cracks having same size) yield to nonuniform crack growth patterns (bifurcation) if λ is larger than a critical value λcr. However, no such bifurcation is found for a collinear crack array under tension. For parallel and edge crack arrays, respectively, the value of λcr decreases monotonically from (2/9)1/2 and (2/15.096)1/2 for arrays of 2 cracks, to (2/3)1/2/π and (2/5.032)1/2/π for infinite arrays of cracks. The critical parameter λcr is calculated numerically for arrays of up to 100 cracks, whilst discrete Fourier transform is used to obtain λcr for infinite crack arrays. For infinite parallel crack arrays under uniaxial compression, a simple shear-induced tensile crack model is formulated and compared to the modified Griffith theory. Based upon the model, λcr can be evaluated numerically depending on μ (the fractional coefficient) and c0/a (c0 and a are the sizes of the shear crack and tensile crack, respectively). As an iterative method is used, no closed form solution is presented. However, the numerical calculations do indicate that λcr decreases with the increase of both μ and c0/a.
URI: http://hdl.handle.net/10397/23450
ISSN: 0376-9429
DOI: 10.1007/BF00035367
Appears in Collections:Journal/Magazine Article

Access
View full-text via PolyU eLinks SFX Query
Show full item record

SCOPUSTM   
Citations

25
Last Week
0
Last month
0
Citations as of Apr 22, 2017

WEB OF SCIENCETM
Citations

16
Last Week
0
Last month
1
Citations as of Apr 19, 2017

Page view(s)

29
Last Week
4
Last month
Checked on Apr 23, 2017

Google ScholarTM

Check

Altmetric



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.