Title: Characterisation and application of nano-scale fibre particles
Authors: Cheng, Yin-fa
Keywords: Hong Kong Polytechnic University -- Dissertations
Textile fibers
Textile fabrics
Textile waste -- Recycling
Nanostructured materials
Issue Date: 2007
Publisher: The Hong Kong Polytechnic University
Abstract: Fibre is a very important material in the textile industry. However, there is a large amount of wastage of fibres generated in textile industry daily. Scientists believe that the development of nanotechnology can allow the reuse of these discarded garments and fibres for creating a great market potential in the textile industry. To achieve this goal, the newly innovative method was proposed for pulverising fibres into nano-scale particles. It was found that the rotate crusher, ultrasonic crusher, ultra-turrax(R) and nano-colliding machine were effective tools for pulverising the fibres including wool, cotton and silk fibres into micro-scale and nano-scale fibres particles. The pulverisation procedures were similar for various fibres except that the pulverisation duration was different. The size of the particles was confirmed to be in micro-scale and nano-scale by means of Scanning Electron Microscopy and Particle Size Analysis. The Fourier Transmittance Infrared Analysis illustrated that the chemical structures of micro-scale and nano-scale fibre particles were only slightly different from those of the original fibres. However, there is a gradual reduction in the crystallinity of the pulverised wool, silk and cotton particles with respect to the decreasing particle size. Attempt had been conducted to coat nano-wool particles onto cotton and polyester fabrics aiming to modify their properties, functions and dyeing performance. The experimental results revealed that nano-wool particles could reduce the air permeability, thermal conductivity, keeping warmth ability, q-max value of both cotton and polyesters fabrics. On the other hand, there was a reduction in the OWTC, OMMC values, moisture management capability and hydrophility for the cotton fabrics, but there was an enhancement in these properties for the polyester fabrics after nano-wool treatment. In addition, the nano-wool treatment also caused the swelling, enhancement in wrinkle recovery and ultraviolet protection of cotton fabrics. In the nano-wool treatment, some parameters such as the amount of nano-wool added, dipping time, curing time and curing temperature did affect the properties and functions of different fabrics in various ways. As for the dyeing performance, it was found that the nano-wool treatment not only increased the colour depth of the dyed cotton and polyester fabrics, but also affected the tone of the dyed fabrics slightly.
Description: xix, 165 leaves : ill. (some col.) ; 30 cm.
PolyU Library Call No.: [THS] LG51 .H577M ITC 2007 Cheng
Rights: All rights reserved.
Appears in Collections:Thesis

Files in This Item:
File Description SizeFormat 
E-thesis_Link.htmFor PolyU Users 161 BHTMLView/Open
b21657610.pdfFor All Users (Non-printable)5.83 MBAdobe PDFView/Open
Show full item record
PIRA download icon_1.1View/Download Contents

Page view(s)

Last Week
Last month
Citations as of Oct 15, 2018


Citations as of Oct 15, 2018

Google ScholarTM


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.