Please use this identifier to cite or link to this item: http://hdl.handle.net/10397/17885
Title: Plasma pretreatment for polymer deposition-improving antifelting properties of wool
Authors: Kan, CW 
Yuen, CWM
Tsoi, WYI
Tang, TB
Keywords: Antifelting
Chlorination
Plasma
Polymer deposition
Surface
Surface modification
Wool fiber
Issue Date: 2010
Publisher: Institute of Electrical and Electronics Engineers
Source: IEEE transactions on plasma science, 2010, v. 38, no. 6 part 2, 5453068, p. 1505-1511 How to cite?
Journal: IEEE transactions on plasma science 
Abstract: Wool substrates of fibers and fabrics were treated with nitrogen plasma under atmospheric pressure or subject to chlorination followed by a polymer deposition process for improving the antifelting property. The antifelting property of wool fibers was assessed by a felting ball test, which revealed that plasma treatment alone could achieve the best antifelting effect, but the hand feel was adversely affected. With the deposition of the polymer on the fiber surface, the antifelting properties were retained with an acceptable hand feel. There was a great improvement in the wettability of the chlorinated and plasma-treated wool fabrics after being qualitatively assessed by wetting time when compared with an untreated fabric sample. The wettability was further quantitatively evaluated through the contact angle measurement with different solvents. The test results showed that the contact angles were reduced implying that the wool surface became more hydrophilic. The SEM pictures showed that a relatively rougher surface was observed for the plasma-treated wool fiber when compared with the chlorinated wool fiber. In addition, X-ray photoelectron spectroscopy (XPS) analysis revealed that there was an increase in oxygen and nitrogen contents of both the chlorinated and plasma-treated wool fibers, which might improve the hydrophilicity of the wool fibers. When the two different surface treatments were compared, the plasma treatment could alter significantly both the physical and chemical surface properties as confirmed by SEM and XPS analyses. However, the chlorination could only alter the surface chemical composition. In conclusion, the improved hydrophilicity of the wool fiber surface by nitrogen plasma could enhance and achieve a better polymer deposition on the wool fiber surface for improving the antifelting properties of wool when compared with the chlorination process.
URI: http://hdl.handle.net/10397/17885
ISSN: 0093-3813 (print)
1939-9375 (online)
DOI: 10.1109/TPS.2010.2046338
Appears in Collections:Journal/Magazine Article

Access
View full-text via PolyU eLinks SFX Query
Show full item record

SCOPUSTM   
Citations

6
Last Week
0
Last month
0
Citations as of Aug 14, 2017

WEB OF SCIENCETM
Citations

6
Last Week
0
Last month
0
Citations as of Aug 12, 2017

Page view(s)

31
Last Week
4
Last month
Checked on Aug 13, 2017

Google ScholarTM

Check

Altmetric



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.