Title: Effects of glass fiber surface modified by nano-SiO2 on mechanical properties of GF/PCBT composites
Authors: Yang, B
Zhang, J
Liang, W
Zhou, L 
Keywords: Fiber pull-out test
Glass fiber
Hygrothermal aging
Polymerized poly(cyclic butylene terephthalate)
Surface modification
Three-point bending test
Vacuum-assisted mold pressing technology
Issue Date: 2015
Publisher: 科学出版社
Source: 复合材料学报 (Acta materiae compositae sinica), 2015, v. 32, no. 3, p. 691-698 How to cite?
Journal: 复合材料学报 (Acta materiae compositae sinica) 
Abstract: To study the effect of glass fiber (GF) surface modified by nano-SiO2 on mechanical properties of GF reinforced matrix composites, vacuum-assisted mold pressing (VAMP) technology was adopted to prepare polymerized poly(cyclic butylene terephthalate)(PCBT)-based composites reinforced by GF modified by various nano-SiO2 on the surface. The effect of GF surface modification on mechanical properties of the obtained GF/PCBT composites was investigated and the hygrothermal aging resistance of GF/PCBT composites with modified GF was further studied. The fiber pull-out test results show that the interface shear strength of GF/PCBT composites enhances by 1.16 times after nano modification on fiber surface. With nano-SiO2 content of 0.5wt%, 2wt% (mass ratio of nano-SiO2 to PCBT), the three-point flexural strength of GF/PCBT composites increases by 1.5 times and 1.67 times, flexural modulus increases by 1.03 times and 1.17 times, respectively. Observations by SEM show that the damaged fibers are covered tightly by PCBT resin when nano-SiO2 content is 2wt%, which is an indication of good bonding properties between the matrix and fibers. Under hygrothermal conditions, hydrone diffusion along the interphase region is hindered and results in the enhancement of the anti-aging performance of the modified GF/PCBT composites, due to the existence of nano-SiO2 particles.
URI: http://hdl.handle.net/10397/15345
ISSN: 1000-3851
DOI: 10.13801/j.cnki.fhclxb.20140611.002
Appears in Collections:Journal/Magazine Article

Access
View full-text via PolyU eLinks SFX Query
Show full item record

SCOPUSTM   
Citations

1
Last Week
0
Last month
0
Citations as of Aug 19, 2017

Page view(s)

72
Last Week
0
Last month
Checked on Aug 21, 2017

Google ScholarTM

Check

Altmetric



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.