Please use this identifier to cite or link to this item: http://hdl.handle.net/10397/11502
Title: Laser surface aluminizing of mild steel : microstructural and corrosion characteristics
Authors: Kwok, CT
Man, HC 
Cheng, FT
Issue Date: 2002
Source: ICALEO 2002 - 21st International Congress on Applications of Laser and Electro-Optics, Congress Proceedings, 2002 How to cite?
Abstract: Laser surface alloying of mild steel AISI 1050 using aluminum alloy (AlFeSi) was attempted. Alloying material in powder form was preplaced on the surface of the substrate by oxyfuel flame spraying. The surface was then consolidated by scanning with a 2-kW CW Nd:YAG laser beam. The micro structures of the alloyed layers were studied by scanning electron microscopy, optical microscopy and X-ray diffractometry. The corrosion and cavitation-erosion characteristics in 3.5% NaCl solution at 23 °C were studied by potentiodynamic polarization technique and by means of a 20 kHz ultrasonic vibratory facility. The laser-alloyed specimens were found to be composed of ferrite and the intermetallic phases Fe3Al, FeAl and Fe 2Al5. The maximum hardness was significantly increased to 595 Hv. The corrosion behaviour was influenced by the degree of dilution of the alloying element. Although aluminizing led to an active shift in the corrosion potential from -510 mV to -890 mV, the specimens showed passivity with pitting and protection potentials of -550 mV and -710 mV respectively while the substrate did not. The corrosion resistance of the laser-alloyed specimens was significantly improved as evidenced by a much lower corrosion current density. In addition, the cavitation-erosion resistance of the laser-alloyed specimens was also significantly improved by 17.7 times that of the substrate due to the increase in both hardness and corrosion resistance of the laser-alloyed layer.
Description: ICALEO 2002 - 21st International Congress on Applications of Laser and Electro-Optics, Scottsdale, AZ, 14-17 October 2002
URI: http://hdl.handle.net/10397/11502
ISBN: 0912035722
9780912035727
Appears in Collections:Conference Paper

Access
View full-text via PolyU eLinks SFX Query
Show full item record

Page view(s)

40
Last Week
1
Last month
Checked on Aug 13, 2017

Google ScholarTM

Check



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.